Product Description
Loaded with features, this economically priced portable hardness tester is capable of measuring the surface hardness of a broad variety of metals on flat and round surfaces. This portable hardness tester comes complete with the G impact device, calibrated test block and rugged carry case.
Designed to test large cast parts and those with rough surfaces: Example: part mass should be equivalent to 1” thick of solid steel where testing.
Operation: • Load the impact body • Place the impact body on your test piece • Push the button to begin testing and obtain reading
Standard Accessories: • Base instrument • Impact device G (“D” PHT-1700, "DL" PHT-1740) • Calibrated test block • Custom carry case • Cleaning brush • Operation manual
Functions: • Easy to use keypad operation • Large LCD display with back light • Automatic conversions to: Brinell, Rockwell, Vickers and Shore • Automatic mean value • Data storage capacity
Specifications: • Accuracy: +/- 0.5% (referred to L=800, • Repeatability accuracy: +/- 4L units) L=Leeb • Measuring range: 200-960 HL • Materials: steel & cast steel, alloy tool steel, stainless steel, grey cast iron, spheroidal iron, cast aluminum, brass, bronze, wrought copper alloy. • Battery type: AAA alkaline (2) • Operating temperature: 5-104 degrees F • Dimensions: 108 x 62 x 25mm • Weight: 230 grams
Options: •NIST/ASTM certified hardness test blocks, penetrators and kits are available.
Impact device ->
G
Impact energy
90Nmm
Mass of the impact body
20g
Test tip
* Hardness
1600HV
* Diameter
5mm
* Material
Tungsten Carbide
Impact device
* Diameter
30mm
* Length
254mm
* Weight
250g
Max. hardness of sample
650HB
Preparation of surface
* Max. roughness depth Rt
30 m m
* Average roughness Ra
6.3 m m
Min. weight of sample
* Of compact shape
15kg
* On solid support
5kg
* Coupled on plate
0. 5kg
Indentation of test tip
With 300 HV
* Diameter
1.03mm
* Depth
53 m m
with 600 HV
* Diameter
0. 90mm
* Depth
41 m m
Designed to test large cast parts and those with rough surfaces: Example: part mass should be equivalent to 1” thick of solid steel where testing.
Operation: • Load the impact body • Place the impact body on your test piece • Push the button to begin testing and obtain reading
Standard Accessories: • Base instrument • Impact device G (“D” PHT-1700, "DL" PHT-1740) • Calibrated test block • Custom carry case • Cleaning brush • Operation manual
Functions: • Easy to use keypad operation • Large LCD display with back light • Automatic conversions to: Brinell, Rockwell, Vickers and Shore • Automatic mean value • Data storage capacity
Specifications: • Accuracy: +/- 0.5% (referred to L=800, • Repeatability accuracy: +/- 4L units) L=Leeb • Measuring range: 200-960 HL • Materials: steel & cast steel, alloy tool steel, stainless steel, grey cast iron, spheroidal iron, cast aluminum, brass, bronze, wrought copper alloy. • Battery type: AAA alkaline (2) • Operating temperature: 5-104 degrees F • Dimensions: 108 x 62 x 25mm • Weight: 230 grams
Options: •NIST/ASTM certified hardness test blocks, penetrators and kits are available.
Impact device ->
G
Impact energy
90Nmm
Mass of the impact body
20g
Test tip
* Hardness
1600HV
* Diameter
5mm
* Material
Tungsten Carbide
Impact device
* Diameter
30mm
* Length
254mm
* Weight
250g
Max. hardness of sample
650HB
Preparation of surface
* Max. roughness depth Rt
30 m m
* Average roughness Ra
6.3 m m
Min. weight of sample
* Of compact shape
15kg
* On solid support
5kg
* Coupled on plate
0. 5kg
Indentation of test tip
With 300 HV
* Diameter
1.03mm
* Depth
53 m m
with 600 HV
* Diameter
0. 90mm
* Depth
41 m m